RESUMO
In this study, the Fe-Mn oxide/mulberry stem biochar composite adsorbent (FM-MBC) was prepared and fully characterized by SEM-EDS, XRD, BET, and XPS. The solution pH (3.0, 4.5, and 6.0), initial concentration of phosphorus (10, 20, and 30 mg L-1), adsorbent bed height (2, 3, and 4 cm), and solution flow rate (1, 2, and 3 mL min-1) were investigated to analyze the breakthrough curves. The results showed that the breakthrough time was shortened as the initial phosphorus concentration, the flow rate increased and the bed height decreased. Higher initial phosphorus concentrations, flow rates, and lower bed heights, led to a faster breakthrough of phosphate ions in the FM-MBC adsorbent. Additionally, it was observed that increasing the pH value was not conducive to the adsorption of phosphorus by the FM-MBC adsorbent. Dynamic adsorption data were fitted to four models (Yoon-Nelson, Thomas, Adams-Bohart, and Bed Depth Service Time), and the R2 values of the Thomas and Yoon-Nelson models exhibited minimal variation, suggesting that the dynamic adsorption process of FM-MBC was rather intricate. The saturated fixed-bed column (including FM-MBC) was regenerated with NaOH or HCl, and it was found that a 0.1 mol L-1 NaOH solution had the best regeneration effect. XRD analysis showed that the reaction product between the FM-MBC composite and phosphate anions was Fe3(PO4)2·H2O. Moreover, the experimental results that FM-MBC can successfully be used to remove phosphorus from actual wastewater.
RESUMO
This study details the preparation of Fe-Mn binary oxide/mulberry stem biochar composite adsorbent (FM-MBC) from mulberry stems via the multiple activation by potassium permanganate, ferrous chloride, triethylenetetramine, and epichlorohydrin. The characteristics of FM-MBC had been characterized by SEM-EDS, BET, FT-IR, XRD, and XPS, and static adsorption batch experiments such as pH, adsorption time, were carried out to study the mechanism of Cr(VI) adsorption on FM-MBC and the impact factors. The results indicated that in contrast with the mulberry stem biochar (MBC), the FM-MBC has more porous on surface with a BET surface area of 74.73 m2/g, and the surface loaded with α-Fe2O3 and amorphization of MnO2 particles. Besides, carboxylic acid, hydroxyl, and carbonyls functional groups were also formed on the FM-MBC surface. At the optimal pH 2.0, the maximum adsorption capacity for Cr(VI) was calculated from the Langmuir model of 28.31, 31.02, and 37.14 mg/g at 25, 35, and 45 °C, respectively. The aromatic groups, carboxyls, and the hydroxyl groups were the mainly functional groups in the adsorption of Cr(VI). The mechanism of the adsorption process of FM-MBC for Cr(VI) mainly involves electrostatic interaction, surface adsorption of Cr(VI) on FM-MBC, and ion exchange.